| Material: | Micro Alloy Steel | Name: | Chrome Piston Rod |
|---|---|---|---|
| Surface Condition: | Chrome Plated | Tensile Strength: | Not Less Than 750 MPa |
| Yield Strength: | Not Less Than 520 N/MM2 | Tolerance On Dia: | F7 |
| High Light: | hollow steel rod,hydraulic cylinder piston rod,hydraulic cylinder chrome piston rod |
||
Tensile Strength > 750 Mpa Chrome Piston Rod For Hydraulic Cylinder
Detailed Product Description
1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700
2. ISO9001:2008
3. Ground and chrome plated
4. Piston rod manufacturer
5. Category: Hard chrome piston rod
Quenched & Tempered (Q+T) rod
Induction hardened rod
Q+T induction hardened rod
Micro alloy steel piston rod
Wind power project piston rod
6. Quality first, Credit principal
Detailed Description
1. CHEMICAL COMPOSITION(%)
|
Material |
C% |
Mn% |
Si% |
S% |
P% |
V% |
Ni |
Cr% |
Mo |
Cu |
|
ck45 |
0.42-0.50 |
0.50-0.80 |
0.17-0.37 |
≤0.035 |
≤0.035 |
|
≤0.25 |
≤0.25 |
|
≤0.25 |
|
ST52 |
≤0.22 |
≤1.6 |
≤0.55 |
≤0.04 |
≤0.04 |
0.02-0.15 |
|
|
|
|
|
20MnV6 |
0.17-0.24 |
1.30-1.70 |
0.10-0.50 |
≤0.035 |
0.035 |
0.10-0.20 |
≤0.30 |
≤0.30 |
|
≤0.30 |
|
42CrMo |
0.38-0.45 |
0.5-0.8 |
0.17-0.37 |
≤0.035 |
≤0.035 |
0.07-0.12 |
≤0.03 |
0.90-1.20 |
0.15-0.25 |
≤0.03 |
|
40Cr |
0.37-0.45 |
0.50-0.80 |
0.17-0.37 |
≤0.035 |
≤0.035 |
|
≤0.3 |
0.80-1.1 |
|
≤0.03 |
|
HY4700 |
0.38-0.45 |
1.20 ~1.60 |
0.30~0.50 |
≤0.035 |
≤0.020 |
0.05～0.15 |
≤0.25 |
0.10～0.20 |
≤0.15 |
0.25 |
|
HY4520 |
0.40 ~0.48 |
0.80 ~1.40 |
0.15 ~0.35 |
≤0.035 |
≤0.035 |
≤0.15 |
≤0.25 |
≤0.25 |
≤0.15 |
≤0.25 |
2. MECHANICAL PROPERTIES
|
Material |
T.S / Rm(MPa) |
Y.S / Rel(MPa) |
A% |
CHARPY |
CONDITION |
|
ck45 |
610 |
355 |
16 |
>41J |
Normalized |
|
ck45 |
800 |
540 |
20 |
>41J |
Q+T |
|
ST52 |
500 |
355 |
22 |
|
Normalized |
|
20MnV6 |
750 |
590 |
12 |
>40J |
Normalized |
|
42CrMo4 |
980 |
850 |
14 |
>47J |
Q+T |
|
40Cr |
1000 |
800 |
10 |
|
Q+T |
3. MICRO ALLOY STEEL
|
Material |
MECHANICAL PROPERTIES |
Surface hardness(HBW) |
|||||
|
Rm(MPa) |
Rel(MPa) |
A% |
Z% |
KU2(J) |
|
||
|
HY4700 |
Φ35 - Φ100 |
900 - 1100 |
≥650 |
≥16 |
≥35 |
≥39 |
270-340 |
|
＞Φ100 - Φ140 |
850 - 950 |
≥600 |
≥16 |
≥35 |
≥39 |
270-340 |
|
|
HY4520 |
Φ40 - Φ100 |
750 - 900 |
≥520 |
≥19 |
≥40 |
≥39 |
230-290 |
|
＞Φ100～Φ140 |
750 - 900 |
≥520 |
≥17 |
≥35 |
≥39 |
230-290 |
|
|
|
|
|
|
|
|
|
|
4. CHROME THICKNESS
20 to 30 micron
5. SUPPLY CONDITION
Ground and chrome plated
6. SURFACE ROUGHNESS
Ra≤0.2 micron and Rt≤2 micron
7. TOLERANCES ON DIA
ISO f7 on the diameter
8.OVALITY
Half of the tolerance ISO f7
9. STRAIGHTNESS
≤0.2MM/M
10 .SURFACE HARDNESS
850-1150HV (vickers 100g)
11. COHESION
No craks,breaking or detaching after thermic shock(warming up at 300 celsius degrees
and cooling in water)
12 .POROSITY
Test according to ISO 1456/1458 and result yaluation according to ISO 4540 rating 8-10
13. CORROSION RESISTANCE
Test in natural salt spray according to ASTM B 117-120hours
Results evaluation according to ISO 4540 RATING 7-10
14. WELDABILITY
Good
15. PACKING
Anti rust oil to be applied on material and each rod to be packed in paper sleeve
16. CERTIFICATE
All certificate related with material heat treatment and plating is required
Contact Person: Miss. Patty
Tel: 8613921505262
Fax: 86-510-83952939