42CrMo4 Kran Piston Dilapisi Tempel dan Tempered Chrome Dengan Kekuatan Tinggi
Atribut Utama
Nama merek:
HY
Tempat Asal:
Cina
Sertifikasi:
ISO9001:2008
Jumlah pesanan minimum:
5 ton
Harga:
negotiable
Kemampuan Penyediaan:
30tons hari
Waktu Pengiriman:
30days
Ketentuan Pembayaran:
L/C, T/T
Standard Packaging:
Anti karat minyak harus diterapkan pada bahan dan setiap batang dikemas dalam kertas lengan
Ringkasan Produk
Quenched Tempered Chrome Plated Piston Rod With 42CrMo4 Product Description 1. Material: 42CrMo4, 40Cr, CK45,ST52, 20MnV6 2. Length: 1000mm - 8000mm 3. Diameter: 6mm - 1000mm 4. Advanced inspection apparatus 5. Complete manufactured equipment Detailed Description 1. Chemical Composition: Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035 ST52 0.22 1.6 0.55 0.035 0.04 20MnV6 0.16-0.22 1.30-1.70 0.10-0.50 0.035 0.035 0.10-0.20 42CrMo4 0.38-0.45 0.60-0.90
Atribut Kustom Produk
Menyoroti
Piston rod berlapis krom bertemperan
,Batang Piston Silinder Hidrolik
,42CrMo4 Plating Chrome Piston Rod
Produk:
Batang piston krom
Pengolahan Permukaan:
Berlapis krom keras
Kekerasan permukaan:
850-1150 HV (vickers 100g)
Lurus:
Tidak lebih dari 0,2 MM/M
Toleransi pada dia:
f7
Ovalitas:
Setengah dari toleransi ISO f7
Deskripsi Produk
Piston rod berlapis krom dengan 42CrMo4
Deskripsi Produk
1Bahan: 42CrMo4, 40Cr, CK45, ST52, 20MnV6
2Panjang: 1000mm - 8000mm
3Diameter: 6mm - 1000mm
4Alat inspeksi canggih
5. Perlengkapan yang diproduksi lengkap
Deskripsi Rinci
1Komposisi kimia:
|
Bahan |
C% |
Mn% |
Si% |
S% |
P% |
V% |
Cr% |
|
Ck45 |
0.42-0.50 |
0.50-0.80 |
0.04 |
0.035 |
0.035 |
|
|
|
ST52 |
0.22 |
1.6 |
0.55 |
0.035 |
0.04 |
|
|
|
20MnV6 |
0.16-0.22 |
1.30-1.70 |
0.10-0.50 |
0.035 |
0.035 |
0.10-0.20 |
|
|
42CrMo4 |
0.38-0.45 |
0.60-0.90 |
0.15-0.40 |
0.03 |
0.03 |
|
0.90-1.20 |
|
40Cr |
0.37-0.45 |
0.50-0.80 |
0.17-0.37 |
|
|
|
0.80-1.10 |
2Sifat Mekanis:
|
Bahan |
T.S N/MM2 |
Y.S N/MM2 |
E% ((MIN) |
CHARPY |
Kondisi |
|
CK45 |
610 |
355 |
15 |
> 41J |
NORMALIZE |
|
CK45 |
800 |
630 |
20 |
> 41J |
Q + T |
|
ST52 |
500 |
355 |
22 |
|
NORMALIZE |
|
20MnV6 |
750 |
590 |
12 |
> 40J |
NORMALIZE |
|
42CrMo4 |
980 |
850 |
14 |
> 47J |
Q + T |
|
40Cr |
1000 |
800 |
10 |
|
Q + T |
3Kondisi pasokan:
| 1 | Berlapis krom keras | ||
| 2 | Induksi mengeras | ||
| 3 | Dipadamkan & Dipanaskan | ||
| 4 | Induksi keras dengan Q&T | ||
4. Kondisi Pasokan
Dihancurkan dan dilapisi krom
5. ketebalan krom
20 sampai 30 mikron
6. Keruwetan permukaan
Ra≤0,2 mikron dan Rt≤2 mikron
7. Toleransi pada hari
ISO f7 pada diameter
8. OVALITY
Setengah dari toleransi ISO f7
9. Kejujuran
≤ 0,2MM/M
10. Kekerasan Permukaan
850-1150HV (Vickers 100g)
11.KOSESI
Tidak ada retakan, pecah atau lepas setelah kelelahan termal (pemanasan di 300 derajat celcius dan pendinginan
dalam air)
12. porositas
Uji menurut ISO 1456/1458 dan evaluasi hasil menurut ISO 4540 rating 8-10
13. ketahanan korosi
Uji dengan semprotan garam alami menurut ASTM B 117-72 jam
Evaluasi hasil menurut ISO 4540 RATING 7-10
14. WELDABILITY
Bagus sekali.
15. Pengemasan
Minyak anti karat yang akan diterapkan pada bahan dan setiap batang yang akan dikemas dalam sleeve kertas
16. CERTIFICATE
Semua sertifikat yang terkait dengan pengolahan panas dan plating bahan diperlukan
FAQ
1.Q: Berapa hari dari pengiriman Anda?
A: Pengiriman umum adalah 30 ~ 50 hari sesuai dengan kuantitas Anda.
2.Q: Apa pasar utama Anda?
A: Kami terutama mengekspor ke Timur Tengah dan Asia Tenggara dan tahun ini produk kami masuk ke Amerika Selatan.
Kami telah mendirikan bengkel baru dan menggunakan peralatan otomatis baru untuk menyelesaikan semua proses.
Produk terkait
Mikro Alloy Steel Chrome Piston Rod Chrome Plating Dengan Kekuatan Tinggi
Micro Alloy Steel Chrome Piston Rod Chrome Plating With High Strength Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700 2. ISO9001:2008 3. Yield strength: Not less than 355 MPa 4. Tensile strength: Not less than 610 MPa 5. Completed manufactured equipments, Advanced inspection apparatus 6. Application: Mining machinery industry, textile / printing industry and so on Detailed Description 1. CHEMICAL COMPOSITION(%) Material C% Mn% Si% S
1m - Panjang 8m Chrome Disepuh Piston Rod, Hydraulic Cylinder Piston Rod
1m - 8m Length Chrome Plated Piston Rod ISO Approved Hydraulic Cylinder Piston Rod Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700 2. Category: Hard chrome piston rod Quenched & Tempered (Q+T) rod Induction hardened rod Q+T induction hardened rod Micro alloy steel piston rod Wind power project piston rod 3. Ground and chrome plated 4. Tensile strength: Not less than 610 MPa 5. Completed manufactured equipments, Advanced inspection apparatus
Kekuatan tarik> 750 Mpa Chrome Piston Rod Untuk Hydraulic Cylinder
Tensile Strength > 750 Mpa Chrome Piston Rod For Hydraulic Cylinder Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700 2. ISO9001:2008 3. Ground and chrome plated 4. Piston rod manufacturer 5. Category: Hard chrome piston rod Quenched & Tempered (Q+T) rod Induction hardened rod Q+T induction hardened rod Micro alloy steel piston rod Wind power project piston rod 6. Quality first, Credit principal Detailed Description 1. CHEMICAL
Super Mesin Hidrolik Piston Rod High Yield Strength
Super Machine Parts Hydraulic Piston Rod High Yield Strength Detailed Product Description 1. Materia for the goods: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, bearing steel, stainless steel.... 2. ISO9001: 2008 3. Ground and chrome plated 4. Piston rod manufacturer 5. Completed manufactured equipments 6. Heyi spirits: Solidarity, Enterprise, Loyalty, Responsibility Detailed Description 1. CHEMICAL COMPOSITION(%) Material C% Mn% Si% S% P% V% Ni Cr% Mo Cu ck45 0.42-0.50 0.50-0.80 0.17
35mm - 140mm Chrome Piston Rod berongga Batang Baja ISO F7 Diameter Toleransi
35mm - 140mm Chrome Piston Rod Hollow Steel Rod ISO F7 Diameter Tolerance Detailed Product Description 1. Materialof the goods: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700 2. Specification length: OD 6mm - 12mm length 1000mm-2000mm OD 16mm-35mm length 2000mm-4000mm OD 40mm-220mm length 4000mm-8000mm OD 250mm-1000mm length 4000mm-8000mm 3. Tensile strength: Not less than 610 N/MM2 4. Yield strength: Not less than 355 N/MM2 5. Advanced inspection apparatus Detailed
Kinerja bagus Chrome Hydraulic Cylinder Rod Panjang 1m - 8m
Great Performance Chrome Hydraulic Cylinder Rod Length 1m - 8m Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700 2. Manufacturer specialized in producing precision long small diameter axes and hydraulic piston rod 3. Ground and chrome plated 4. Application: Mining machinery industry, textile / printing industry and so on 5. Diameter: 6mm - 1000mm, Length: 1000mm-8000mm Detailed Description 1. CHEMICAL COMPOSITION(%) Material C% Mn% Si
42CrMo4 Keras Chrome Piston Rod Quenching / Tempered untuk Hydraulic Cylinder
42CrMo4 Hard Chrome Piston Rod Quenched / Tempered for Hydraulic Cylinder Detailed Product Description 1. Material:CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Diameter: 6~1000mm 3. length: 1000~8000mm 4. Hard chrome plated 5. Piston rod manufacturer Detailed Description 1. CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035 ST52 0.22 1.6 0.55 0.035 0.04 20MnV6 0.16-0.22 1.30-1.70 0.10-0.50 0.035 0.035 0.10-0.20 42CrMo4 0.38-0.45 0.60-0.90
Hidrolik silinder Induksi Hardened Rod 1000mm - 8000mm Panjang
Hydraulic Cylinder Induction Hardened Rod 1000mm - 8000mm Length Product Description 1. Material: 42CrMo4, 40Cr, CK45,ST52, 20MnV6 2. Length: 1000mm - 8000mm 3. Diameter: 6mm - 1000mm 4. Tensile strength: Not less than 610 N/MM2 5. Yield strength: Not less than 355 N/MM2 Detailed Description 1. Chemical Composition: Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035 ST52 0.22 1.6 0.55 0.035 0.04 20MnV6 0.16-0.22 1.30-1.70 0.10-0.50 0.035 0.035 0.10-0