42CrMo4, 40Cr, 20MnV6 Bulat Induksi Harded Steel Rod / Bar Untuk Mesin Berat
Atribut Utama
Nama merek:
HY
Tempat Asal:
Cina
Sertifikasi:
ISO9001:2008
Jumlah pesanan minimum:
1 ton
Harga:
negotiable
Kemampuan Penyediaan:
30tons hari
Waktu Pengiriman:
30days
Ketentuan Pembayaran:
L/C, T/T
Standard Packaging:
Anti karat minyak harus diterapkan pada bahan dan setiap batang dikemas dalam kertas lengan
Ringkasan Produk
42CrMo4, 40Cr, 20MnV6 Round Induction Hardened Steel Rod/Bar For Heavy Machine Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Ground and chrome plated 3. ISO9001:2008 4. Complete manufactured equipment 5. Condition: Chrome plated, Quenched / Tempered, Induction hardened, Q / T Induction hardened 6. Case depth:1.5mm - 2.5mm Induction hardness: HRC50 - 60 Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50
Atribut Kustom Produk
Menyoroti
20MnV6 baja tahan karat
,Rod baja pengeras induksi bulat
,Batang Baja yang Dikeras Mesin Berat
Nama:
Batang yang dikeraskan dengan induksi krom
Bahan baku:
Baja tahan karat, baja karbon
Diameter:
6mm - 1000mm
Panjang:
1000mm - 8000mm
kondisi permukaan:
Pelapisan Chrome Keras
Ketebalan krom:
20-30 mikron
Deskripsi Produk
42CrMo4, 40Cr, 20MnV6 Putaran Induksi Hardened Batang Baja / Bar Untuk Mesin Berat
Detil Deskripsi Produk
1. Bahan: CK45, ST52, 20MnV6, 42CrMo4, 40Cr
2. Tanah dan berlapis krom
3. ISO9001: 2008
4. peralatan diproduksi Lengkap
5. Kondisi: Chrome berlapis, Dikuens / Tempered, Induksi mengeras, Q / T Induksi mengeras
6. Kasus kedalaman: 1.5mm - 2.5mm Induksi kekerasan: HRC50 - 60
Detil Deskripsi
KOMPOSISI 1.Chemical
Bahan | C% | M N% | Si% | S% | P% | V% | cr% |
Ck45 | 0,42-0,50 | 0,50-0,80 | 0.04 | 0,035 | 0,035 | ||
ST52 | 0.22 | 1.6 | 0.55 | 0,035 | 0.04 | ||
20MnV6 | 0,16-0,22 | 1,30-1,70 | 0,10-0,50 | 0,035 | 0,035 | 0,10-0,20 | |
42CrMo4 | 0,38-0,45 | 0,60-0,90 | 0,15-0,40 | 0.03 | 0.03 | 0,90-1,20 | |
40Cr | 0,37-0,45 | 0,50-0,80 | 0,17-0,37 | 0,80-1,10 |
SIFAT 2.MECHANCIAL
Bahan | TS N / MM2 | YS N / MM2 | E% (MIN) | Charpy | KONDISI |
CK45 | 610 | 355 | 15 | > 41J | menormalkan |
CK45 | 800 | 630 | 20 | > 41J | Q + T |
ST52 | 500 | 355 | 22 | menormalkan | |
20MnV6 | 750 | 590 | 12 | > 40J | menormalkan |
42CrMo4 | 980 | 850 | 14 | > 47J | Q + T |
40Cr | 1000 | 800 | 10 | Q + T |
3. SUPPLY KONDISI
Tanah dan berlapis krom
4. CHROME TEBAL
20 sampai 30 mikron
5. KEKASARAN PERMUKAAN
Ra≤0.2 mikron dan Rt≤2 mikro
6. TOLERANSI ON DIA
ISO f7 pada diameter
7.OVALITY
Setengah dari toleransi ISO f7
8. kelurusan
≤0.2MM / M
9. PERMUKAAN KEKERASAN
850-1150HV (vickers 100g)
10.COHESION
Tidak ada retak, pecah atau melepaskan setelah syok termal (pemanasan pada 300 derajat celsius dan pendinginan
dalam air)
11 .POROSITY
Uji sesuai dengan ISO 1456/1458 dan menghasilkan yaluation sesuai dengan ISO 4540 Peringkat 8-10
12 karat
Tes di semprot garam alami menurut 117-72hours ASTM B
Evaluasi hasil sesuai dengan ISO 4540 RATING 7-10
13. mampu las
Baik
14. KEMASAN
Anti minyak karat untuk diterapkan pada bahan dan setiap batang akan dikemas dalam lengan kertas
15. SERTIFIKAT
Semua sertifikat terkait dengan perlakuan panas material dan plating diperlukan
Kami diimpor kontinyu garis chrome plating dari Italia pada awal 2016. Dengan baris ini chrome plating baru, kita akan meningkatkan efisiensi dan kualitas produk banyak. Garis chrome plating baru adalah yang pertama di Cina dan akan menjadi satu-satunya dalam lima tahun ke depan!
Produk terkait
CK45 42CrMo 20MnV6 40Cr Induksi Hardened Bar Dengan F7 Toleransi
High Quality Induction Hardened Bar 42CrMo With F7 Tolerance Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Diameter: 6mm - 1000mm 3. Length: 1000mm - 8000mm 4. Advanced inspection apparatus 5. Application: Mining machinery industry, textile / printing industry and so on 6. Case depth:1.2mm - 2.5mm Induction hardness: HRC52 - 58 Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0
Induksi Hardened Chrome Disepuh Bar HRC52-58 Bahan CK45 Untuk Mesin Berat
Induction Hardened Chrome Plated Bar HRC52-58 Material CK45 For Heavy Machines Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Diameter: 6mm - 1000mm 3. Length: 1000mm - 8000mm 4. Advanced inspection apparatus 5. Application: Mining machinery industry, textile / printing industry and so on 6. Case depth:1.2mm - 2.5mm Induction hardness: HRC52 - 58 Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0
Induksi dipadamkan / marah mengeras baja Bar untuk silinder hidrolik
Quenched / Tempered Induction Hardened Steel Bar For Hydraulic Cylinder Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Ground and chrome plated 3. ISO9001:2008 4. Advanced inspection apparatus 5. Application: Mining machinery industry, textile / printing industry and so on 6. Case depth:1.5mm - 2.5mm Induction hardness: HRC50 - 60 Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0
Heat Treatment Induksi Hardened Bar Untuk Hydraulic Cylinder
Heat Treatment Induction Hardened Bar For Hydraulic Cylinder Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Ground and chrome plated 3. ISO9001:2008 4. Condition: Chrome plated, Quenched / Tempered, Induction hardened, Q / T Induction hardened 5. Application: Mining machinery industry, textile / printing industry and so on 6. Case depth:1.5mm - 2.5mm Induction hardness: HRC50 - 60 Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si%
Induksi Hardened Batang Baja Chrome Plating Untuk Hydraulic Cylinder
Induction Hardened Steel Rod Chrome Plating For Hydraulic Cylinder Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Tensile strength: Not less than 610 N/MM2 3. Yield strength: Not less than 355 N/MM2 4. Complete manufactured equipment 5. Application: Mining machinery industry, textile / printing industry and so on 6. Case depth:1.5mm - 2.5mm Induction hardness: HRC50 - 60 Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V%
Kekuatan tinggi Hardened Bar Dengan Quenching / Tempered 42CrMo4, 40Cr
High Strength Hardened Bar With Quenched / Tempered 42CrMo4 , 40Cr Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Diameter: 6mm - 1000mm 3. Length: 1000mm - 8000mm 4. Tensile strength: Not less than 610 N/MM2 5. Yield strength: Not less than 355 N/MM2 6. Case depth:1.5mm - 2.5mm Induction hardness: HRC50 - 60 Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035 ST52 0.22 1.6 0.55
42CrMo4 Induksi Hardened Bar Quenching / Tempered Rod Chrome Plating
42CrMo4 Induction Hardened Bar Quenched / Tempered Rod Chrome Plating Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Diameter: 6mm - 1000mm 3. Length: 1000mm - 8000mm 4. Advanced inspection apparatus 5. Application: Mining machinery industry, textile / printing industry and so on 6. Case depth:1.5mm - 2.5mm Induction hardness: HRC50 - 60 Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0
Baja Induksi Hardened Bar, Hydraulic Piston Rod Untuk industri
Steel Induction Hardened Bar , Hydraulic Piston Rod For industry Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Tensile strength: Not less than 610 N/MM2 3. Yield strength: Not less than 355 N/MM2 4. Advanced inspection apparatus 5. Application: Mining machinery industry, textile / printing industry and so on 6. Case depth:1.5mm - 2.5mm Induction hardness: HRC50 - 60 Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr%