Batang Penghubung Piston Berongga Baja 42CrMo4, Bar Berongga Chrome Tahan Aus

Atribut Utama

Nama merek: HY

Tempat Asal: Cina

Sertifikasi: ISO9001:2008

Jumlah pesanan minimum: 1 ton

Harga: negotiable

Kemampuan Penyediaan: 30 ton sehari

Waktu Pengiriman: 30 hari

Ketentuan Pembayaran: T/T, L/C

Standard Packaging: Minyak anti karat dioleskan pada bahan dan setiap batang dikemas dalam selongsong kertas

Ringkasan Produk

Steel Hollow Piston Rod For Hydraulic Cylinder For CNC Gear-Cutting Machinery The piston rod material 42CrMo4V hardened and hard chrome plated with the material number 1.7225 is suitable for heavy use and is especially wear-resistant thanks to its hardened surface layer with a surface hardness of 56–64 HRC. Due to the material's high stability very high forces can be transmitted, e.g. for small connecting threads with large piston rods. Hard chrome plating means that an

Atribut Kustom Produk

Menyoroti

Batang penghubung piston 42CrMo4

,

batang berongga krom 42CrMo4

,

batang berongga krom tahan aus

Fitur:

Tahan korosi

Bahan:

42CrMo4

Produk:

Batang piston berlapis krom

Ketebalan krom:

20-30 mikron

Kekasaran permukaan:

Ra0.2

Toleransi diameter:

f7

Deskripsi Produk

Batang Piston Berongga Baja Untuk Silinder Hidrolik Untuk Mesin Pemotong Gigi CNC

Bahan batang piston 42CrMo4V mengeras dan berlapis krom keras dengan nomor bahan 1.7225 cocok untuk penggunaan berat dan sangat tahan aus berkat lapisan permukaannya yang diperkeras dengan kekerasan permukaan 56–64 HRC.Karena stabilitas material yang tinggi, gaya yang sangat tinggi dapat ditransmisikan, misalnya untuk ulir penghubung kecil dengan batang piston besar.Pelapisan krom keras berarti lapisan krom yang sangat tebal diterapkan setelah pra-pengasahan dan sebelum menyelesaikan proses mengasah.Ketebalan lapisan tergantung pada diameter batang dan memiliki kekerasan lebih dari 800 HV.Batang piston berlapis krom keras dapat digunakan antara -15°C dan 200°C.

Fitur Batang Piston Chrome

Batang Piston Berlapis Chrome Keras dibuat menggunakan bahan baku berkualitas optimal dan mesin terbaru.Batang menjalani proses yang ketat seperti pilling, pelurusan, penggilingan, pemolesan, pelapisan krom keras, dan finishing di bawah pengawasan insinyur berpengalaman.

Batang Piston Berlapis Chrome Keras banyak digunakan dalam silinder hidrolik dan pneumatik, mesin cetak, mesin tekstil, mesin teknik, mesin pertukangan kayu, dll. Produk kami sangat dihargai oleh klien kami karena fitur mereka seperti ketahanan korosi, konstruksi yang kuat, daya tahan yang tinggi, tinggi kekuatan tarik dan permukaan seperti cermin.

Batang Piston ChromeKeterangan
1. Bahan: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700
2.ISO9001:2008

3. Kekuatan hasil: Tidak kurang dari 355 MPa
4. Kekuatan tarik: Tidak kurang dari 610 MPa
5. Menyelesaikan peralatan yang diproduksi, peralatan inspeksi lanjutan

6.Aplikasi: Industri mesin pertambangan, industri tekstil/percetakan, dan sebagainya

Batang Piston ChromeDetil Deskripsi

1. KOMPOSISI KIMIA (%)

Bahan	C%	M N%	Si%	S%	P%	V%	Ni	Kr%	Mo	Cu
ck45	0,42-0,50	0,50-0,80	0,17-0,37	≤0,035	≤0,035		≤0,25	≤0,25		≤0,25
ST52	≤0,22	≤1.6	≤0,55	≤0,04	≤0,04	0,02-0,15
20MnV6	0,17-0,24	1.30-1.70	0,10-0,50	≤0,035	0,035	0,10-0,20	≤0,30	≤0,30		≤0,30
42CrMo	0,38-0,45	0,5-0,8	0,17-0,37	≤0,035	≤0,035	0,07-0,12	≤0,03	0,90-1,20	0,15-0,25	≤0,03
40Cr	0,37-0,45	0,50-0,80	0,17-0,37	≤0,035	≤0,035		≤0,3	0,80-1,1		≤0,03
HY4700	0,38-0,45	1,20 ~ 1,60	0,30~0,50	≤0,035	≤0.020	0,05～0,15	≤0,25	0,10～0,20	≤0,15	0,25
HY4520	0,40 ~ 0,48	0,80 ~ 1,40	0,15 ~ 0,35	≤0,035	≤0,035	≤0,15	≤0,25	≤0,25	≤0,15	≤0,25

SIFAT MEKANIS Batang Piston Chrome

Bahan	TS / Rm(MPa)	YS / Rel(MPa)	SEBUAH%	CHARPY	KONDISI
ck45	610	355	16	>41J	Dinormalisasi
ck45	800	540	20	>41J	Q+T
ST52	500	355	22		Dinormalisasi
20MnV6	750	590	12	>40J	Dinormalisasi
42CrMo4	980	850	14	>47J	Q+T
40Cr	1000	800	10		Q+T

Batang Piston Chrome BAJA PADUAN MIKRO

Bahan		PERALATAN MEKANIS					Kekerasan permukaan (HBW)
Bahan		Rm(MPa)	Rel(MPa)	SEBUAH%	Z%	KU2(J)
HY4700	Φ35 - Φ100	900 - 1100	≥650	≥16	≥35	≥39	270-340
HY4700	＞Φ100 - Φ140	850 - 950	≥600	≥16	≥35	≥39	270-340
HY4520	Φ40 - Φ100	750 - 900	≥520	≥19	≥40	≥39	230-290
HY4520	＞Φ100～Φ140	750 - 900	≥520	≥17	≥35	≥39	230-290

KONDISI PERSEDIAANTanah dan berlapis krom
KETEBALAN CHROME20 sampai 30 mikron
KEKASARAN PERMUKAANRa≤0,2 mikron dan Rt≤2 mikron
TOLERANSION DIA ISO f7 pada diameter
KualitasSetengah dari toleransi ISO f7
KELURUSAN≤0.2MM/M
KEKERASAN PERMUKAAN850-1150HV (vickers 100g)
KOHESITidak retak, pecah atau terlepas setelah kejutan termal (pemanasan pada 300 derajat celsius dan pendinginan dalam air)
TAHAN KOROSIUji dalam semprotan garam alami menurut ASTM B 117-120 jam Evaluasi hasil menurut ISO 4540 PERINGKAT 7-10
POROSITASTes menurut ISO 1456/1458 dan hasil yaluasi menurut ISO 4540 rating 8-10
KEMAMPUAN LASBagus
SEDANG MENGEMASMinyak anti karat dioleskan pada bahan dan setiap batang dikemas dalam selongsong kertas
SERTIFIKATSemua sertifikat yang terkait dengan perlakuan panas material dan pelapisan diperlukan

Memenuhi kebutuhan klien adalah tujuan kami selamanya.

Saling menguntungkan dan maju bergandengan tangan.

Batang Penghubung Piston Berongga Baja 42CrMo4, Bar Berongga Chrome Tahan Aus 0

Tag

batang baja berongga

silinder hidrolik batang piston

krom hidrolik batang silinder

Produk terkait

Mikro Alloy Steel Chrome Piston Rod Chrome Plating Dengan Kekuatan Tinggi

Micro Alloy Steel Chrome Piston Rod Chrome Plating With High Strength Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700 2. ISO9001:2008 3. Yield strength: Not less than 355 MPa 4. Tensile strength: Not less than 610 MPa 5. Completed manufactured equipments, Advanced inspection apparatus 6. Application: Mining machinery industry, textile / printing industry and so on Detailed Description 1. CHEMICAL COMPOSITION(%) Material C% Mn% Si% S

1m - Panjang 8m Chrome Disepuh Piston Rod, Hydraulic Cylinder Piston Rod

1m - 8m Length Chrome Plated Piston Rod ISO Approved Hydraulic Cylinder Piston Rod Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700 2. Category: Hard chrome piston rod Quenched & Tempered (Q+T) rod Induction hardened rod Q+T induction hardened rod Micro alloy steel piston rod Wind power project piston rod 3. Ground and chrome plated 4. Tensile strength: Not less than 610 MPa 5. Completed manufactured equipments, Advanced inspection apparatus

Kekuatan tarik> 750 Mpa Chrome Piston Rod Untuk Hydraulic Cylinder

Tensile Strength > 750 Mpa Chrome Piston Rod For Hydraulic Cylinder Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700 2. ISO9001:2008 3. Ground and chrome plated 4. Piston rod manufacturer 5. Category: Hard chrome piston rod Quenched & Tempered (Q+T) rod Induction hardened rod Q+T induction hardened rod Micro alloy steel piston rod Wind power project piston rod 6. Quality first, Credit principal Detailed Description 1. CHEMICAL

Super Mesin Hidrolik Piston Rod High Yield Strength

Super Machine Parts Hydraulic Piston Rod High Yield Strength Detailed Product Description 1. Materia for the goods: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, bearing steel, stainless steel.... 2. ISO9001: 2008 3. Ground and chrome plated 4. Piston rod manufacturer 5. Completed manufactured equipments 6. Heyi spirits: Solidarity, Enterprise, Loyalty, Responsibility Detailed Description 1. CHEMICAL COMPOSITION(%) Material C% Mn% Si% S% P% V% Ni Cr% Mo Cu ck45 0.42-0.50 0.50-0.80 0.17

35mm - 140mm Chrome Piston Rod berongga Batang Baja ISO F7 Diameter Toleransi

35mm - 140mm Chrome Piston Rod Hollow Steel Rod ISO F7 Diameter Tolerance Detailed Product Description 1. Materialof the goods: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700 2. Specification length: OD 6mm - 12mm length 1000mm-2000mm OD 16mm-35mm length 2000mm-4000mm OD 40mm-220mm length 4000mm-8000mm OD 250mm-1000mm length 4000mm-8000mm 3. Tensile strength: Not less than 610 N/MM2 4. Yield strength: Not less than 355 N/MM2 5. Advanced inspection apparatus Detailed

Kinerja bagus Chrome Hydraulic Cylinder Rod Panjang 1m - 8m

Great Performance Chrome Hydraulic Cylinder Rod Length 1m - 8m Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr, HY4520, HY4700 2. Manufacturer specialized in producing precision long small diameter axes and hydraulic piston rod 3. Ground and chrome plated 4. Application: Mining machinery industry, textile / printing industry and so on 5. Diameter: 6mm - 1000mm, Length: 1000mm-8000mm Detailed Description 1. CHEMICAL COMPOSITION(%) Material C% Mn% Si

42CrMo4 Keras Chrome Piston Rod Quenching / Tempered untuk Hydraulic Cylinder

42CrMo4 Hard Chrome Piston Rod Quenched / Tempered for Hydraulic Cylinder Detailed Product Description 1. Material:CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Diameter: 6~1000mm 3. length: 1000~8000mm 4. Hard chrome plated 5. Piston rod manufacturer Detailed Description 1. CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035 ST52 0.22 1.6 0.55 0.035 0.04 20MnV6 0.16-0.22 1.30-1.70 0.10-0.50 0.035 0.035 0.10-0.20 42CrMo4 0.38-0.45 0.60-0.90

Hidrolik silinder Induksi Hardened Rod 1000mm - 8000mm Panjang

Hydraulic Cylinder Induction Hardened Rod 1000mm - 8000mm Length Product Description 1. Material: 42CrMo4, 40Cr, CK45,ST52, 20MnV6 2. Length: 1000mm - 8000mm 3. Diameter: 6mm - 1000mm 4. Tensile strength: Not less than 610 N/MM2 5. Yield strength: Not less than 355 N/MM2 Detailed Description 1. Chemical Composition: Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035 ST52 0.22 1.6 0.55 0.035 0.04 20MnV6 0.16-0.22 1.30-1.70 0.10-0.50 0.035 0.035 0.10-0

Chrome Piston Rod

Berongga Piston Rod

Hidrolik Piston Rods

Sulit Chrome Disepuh Rod

Baja yang Dapat Dilakukan di Rod

Sulit Chrome Disepuh Bar

Berongga Logam Rod

Hampa Round Bar

Induksi Hardened Rod

Induksi mengeras Bar

Kustom dasi Rod

Diasah Tabung

Pneumatic Piston Rod

Hydraulic Cylinder Rod

Presisi Baja Shaft

Mikro baja paduan