AISI4140 CK45 Batang Berlapis Krom Keras Silinder Hidrolik 1000mm
Atribut Utama
Nama merek:
HY
Tempat Asal:
Cina
Sertifikasi:
ISO9001:2008
Jumlah pesanan minimum:
5 ton
Harga:
negotiable
Kemampuan Penyediaan:
30 ton sehari
Waktu Pengiriman:
30 hari
Ketentuan Pembayaran:
CIF, FOB atau lainnya
Standard Packaging:
Minyak anti karat untuk diaplikasikan pada material dan setiap batang untuk dikemas dalam selongsong
Ringkasan Produk
AISI4140 CK45 Hard Chrome Plated Rod Hydraulic Cylinder Rod Detailed Product Description Material: CK45, SAE1045, 4140, 4340, JIS45C, 40Cr, 42CrMo Diameter: Φ 6-500 mm Length: max 16m Chrome layer: 20 microns (min) The hardness of the chrome layer: 800HV-1150HV Roughness: Ra ≤0.2u Straightness: ≤ 0.2/1000 Diameter tolerance: ISO f7 Roundness: the deviation of roundness is 50% of the diameter tolerance at the most. Supply condition: Hard chrome plated/ Hardened and tempered/
Atribut Kustom Produk
Menyoroti
Batang Krom Silinder Hidrolik
,Batang Berlapis Krom AISI4140
,Batang Berlapis Krom Keras CK45
Nama:
Batang Berlapis Krom Keras
panjangnya:
1000mm - 8000mm
Diameter:
6mm - 1000mm
Toleransi Diameter:
ISO f7
Pengobatan permukaan:
Berlapis krom keras
Kekuatan hasil:
Tidak kurang dari 355 N/MM2
Deskripsi Produk
AISI4140 CK45 Batang Berlapis Krom Keras Batang Silinder Hidrolik
Deskripsi Produk Rinci
- Bahan: CK45, SAE1045, 4140, 4340, JIS45C, 40Cr, 42CrMo
- Diameter: 6-500 mm
- Panjang: maks 16m
- Lapisan Chrome: 20 mikron (menit)
- Kekerasan lapisan krom: 800HV-1150HV
- Kekasaran: Ra 0.2u
- Lurus: 0.2/1000
- Toleransi diameter: ISO f7
- Kebulatan: penyimpangan kebulatan paling banyak 50% dari toleransi diameter.
- Kondisi pasokan: Berlapis krom keras / Dikeraskan dan ditempa / Induksi mengeras
- Pengemasan: Minyak anti karat untuk disebarkan pada permukaan batang dan setiap batang dikemas dalam gulungan kertas dan kemudian dalam kotak kayu.
Detil Deskripsi
1. KOMPOSISI KIMIA
|
Bahan |
C% |
M N% |
Si% |
S% |
P% |
V% |
Cr% |
|
Ck45 |
0,42-0,50 |
0.50-0.80 |
0,04 |
0,035 |
0,035 |
|
|
|
ST52 |
0,22 |
1.6 |
0,55 |
0,035 |
0,04 |
|
|
|
20MnV6 |
0,16-0,22 |
1.30-1.70 |
0.10-0.50 |
0,035 |
0,035 |
0.10-0.20 |
|
|
42CrMo4 |
0,38-0,45 |
0.60-0.90 |
0,15-0,40 |
0,03 |
0,03 |
|
0,90-1,20 |
|
40Cr |
0,37-0,45 |
0.50-0.80 |
0,17-0,37 |
|
|
|
0,80-1,10 |
2. SIFAT MEKANIAL
|
Bahan |
TS N/MM2 |
YS N/MM2 |
E%(MIN) |
CHARPY |
KONDISI |
|
CK45 |
610 |
355 |
15 |
>41J |
NORMALISASI |
|
CK45 |
800 |
630 |
20 |
>41J |
Q + T |
|
ST52 |
500 |
355 |
22 |
|
NORMALISASI |
|
20MnV6 |
750 |
590 |
12 |
>40J |
NORMALISASI |
|
42CrMo4 |
980 |
850 |
14 |
>47J |
Q + T |
|
40Cr |
1000 |
800 |
10 |
|
Q + T |
3. KONDISI PERSEDIAAN
Tanah dan berlapis krom
4. KETEBALAN CHROME
20 hingga 30 mikron
5. KEKASARAN PERMUKAAN
Ra≤0.2 mikron dan Rt≤2 mikro
6. TOLERANSI PADA DIA
ISO f7 pada diameter
7.OVALITAS
Setengah dari toleransi ISO f7
8. KELULUSAN
0.2MM/M
9. KEKERASAN PERMUKAAN
850-1150HV (vickers 100g)
10.KOHESI
Tidak ada retak, pecah atau terlepas setelah kejutan termal (pemanasan pada 300 derajat celsius dan pendinginan
dalam air)
11. POROSITAS
Uji menurut ISO 1456/1458 dan hasil yaluasi menurut peringkat ISO 4540 8-10
12 KETAHANAN KOROSI
Uji dalam semprotan garam alami menurut ASTM B 117-72 jam
Hasil evaluasi menurut ISO 4540 RATING 7-10
13. KEMAMPUAN LAS
Bagus
14. KEMASAN
Minyak anti karat untuk diaplikasikan pada material dan setiap batang untuk dikemas dalam selongsong kertas
15. SERTIFIKAT
Semua sertifikat yang terkait dengan perlakuan panas dan pelapisan material diperlukan
Ide layanan kami: Dikhususkan untuk kedua manfaat adalah gaya kami yang gigih, Memuaskan kebutuhan klien adalah pengejaran abadi kami
Target Heyi: menjadi patokan di bidang batang piston pneumatik dan hidrolik China
Produk terkait
Mikro Alloy Steel Keras Chrome Bar Disepuh / Kekuatan Tinggi Chrome Disepuh Tubing
Micro Alloy Steel Hard Chrome Plated Bars With High Strength For Hydraulic Cylinder Detailed Product Description 1. Material: CK45, 20MnV6, ST52, 42CrMo4, 40Cr, HY4520, HY4700 2. Professional piston rod manufacturer 3. Yield strength: Not less than 355 MPa 4. Tensile strength: Not less than 610 MPa 5. High quality, good reputation 6. Application: Mining machinery industry, textile / printing industry and so on Detailed Description 1. CHEMICAL COMPOSITION(%) Material C% Mn% Si
CK45 Keras Chrome Disepuh Rod Untuk Hydraulic Cylinder, Tempered Rod
CK45 Hard Chrome Plated Rod For Hydraulic Cylinder , Tempered Rod Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Length: 1000~8000mm 3. Diameter: 6~1000mm 4. Ground and chrome plated 5. ISO9001:2008 Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035 ST52 0.22 1.6 0.55 0.035 0.04 20MnV6 0.16-0.22 1.30-1.70 0.10-0.50 0.035 0.035 0.10-0.20 42CrMo4 0.38-0.45 0.60-0.90 0.15-0.40 0
CK45 Chrome Disepuh Hydraulic Cylinder Shaft Induksi Hardened
CK45 Chrome Plated Hydraulic Cylinder Shaft Induction Hardened Detailed Product Description 1. Material: 42CrMo4, 40Cr, CK45,ST52, 20MnV6 2. Ground and chrome plated 3. Complete manufactured equipment 4. Condition: Chrome plated, Quenched / Tempered, Induction hardened, Q / T Induction hardened 5. Application: Mining machinery industry, textile / printing industry and so on Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0
Presisi Keras Chrome Disepuh Rod Stainless Steel Untuk Cylinder
Precision Hard Chrome Plated Rod Stainless Steel For Cylinder Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Length: 1000~8000mm 3. Diameter: 6~1000mm 4. Advanced inspection apparatus 5. Condition: Chrome plated, Quenched / Tempered, Induction hardened, Q / T Induction hardened Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035 ST52 0.22 1.6 0.55 0.035 0.04 20MnV6 0.16-0.22 1
Profesional Induksi Hardened Chrome Bar / Dingin Diambil Baja Bar
Professional Induction Hardened Chrome Bar / Cold Drawn Steel Bar Detailed Product Description 1. Material: 42CrMo4, 40Cr, CK45,ST52, 20MnV6 2. Advanced inspection apparatus 3. Complete manufactured equipment 4. Condition: Chrome plated, Quenched / Tempered, Induction hardened, Q / T Induction hardened 5. Application: Mining machinery industry, textile / printing industry and so on Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0
Dipadamkan / Tempered Keras Chrome Disepuh Rod Untuk Hydraulic Cylinder Diameter 6-1000mm
Quenched / Tempered Hard Chrome Plated Rod For Hydraulic Cylinder Diameter 6-1000mm Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Length: 1000~8000mm 3. Diameter: 6~1000mm 4. Advanced inspection apparatus 5. ISO9001:2008 Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035 ST52 0.22 1.6 0.55 0.035 0.04 20MnV6 0.16-0.22 1.30-1.70 0.10-0.50 0.035 0.035 0.10-0.20 42CrMo4 0.38-0.45
Profesional Chrome Disepuh Baja Bar Kekuatan Tinggi Untuk Cr-plating Piston
Professional Chrome Plated Steel Bar High Strength For Cr-plating Piston Detailed Product Description 1. Material: 42CrMo4, 40Cr, CK45,ST52, 20MnV6 2. Ground and chrome plated 3. Advanced inspection apparatus 4. Complete manufactured equipment 5. Condition: Chrome plated, Quenched / Tempered, Induction hardened, Q / T Induction hardened Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035 ST52 0.22 1.6 0.55 0
CK45 / 20MnV6 Keras Chrome Disepuh Rod / Hydraulic Cylinder Shaft
CK45 / 20MnV6 Hard Chrome Plated Rod / Hydraulic Cylinder Shaft Detailed Product Description 1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr 2. Length: 1000~8000mm 3. Diameter: 6~1000mm 4. Ground and chrome plated 5. Advanced inspection apparatus Detailed Description 1.CHEMICAL COMPOSITION Material C% Mn% Si% S% P% V% Cr% Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035 ST52 0.22 1.6 0.55 0.035 0.04 20MnV6 0.16-0.22 1.30-1.70 0.10-0.50 0.035 0.035 0.10-0.20 42CrMo4 0.38-0.45 0.60-0