Induction Hardened Steel Rod Chrome Plating For Hydraulic Cylinder

1. Material: CK45, ST52, 20MnV6, 42CrMo4, 40Cr

2. Tensile strength: Not less than 610 N/MM2

3. Yield strength: Not less than 355 N/MM2

4. Complete manufactured equipment

5. Application: Mining machinery industry, textile / printing industry and so on

6. Case depth:1.5mm - 2.5mm  Induction hardness: HRC50 - 60

Detailed Description

1.CHEMICAL COMPOSITION

2.MECHANCIAL PROPERTIES

3. SUPPLY CONDITION

    Ground  and  chrome plated 

4. CHROME THICKNESS

     20 to 30 micron

5. SURFACE ROUGHNESS

     Ra≤0.2 micron and  Rt≤2 micro

6. TOLERANCES ON DIA

    ISO f7 on the diameter

7.OVALITY

   Half of the tolerance ISO f7

8. STRAIGHTNESS

   ≤0.2MM/M

9. SURFACE HARDNESS

   850-1150HV (vickers 100g)

10.COHESION

   No cracks,breaking or detaching after thermic shock(warming up at 300 celsius degrees and cooling 

   in water)

11 .POROSITY

     Test according to ISO 1456/1458 and result yaluation according to ISO 4540 rating 8-10

12 CORROSION RESISTANCE

     Test in natural salt spray according to ASTM B 117-72hours

     Results evaluation according to ISO 4540 RATING 7-10

13. WELDABILITY

      Good

14. PACKING

     Anti rust oil to be applied on material and each rod to be packed in paper sleeve

15. CERTIFICATE

     All certificate related with material heat treatment and plating is required

From 2016, we have imported continous chrome plating line from Italy which is the first one in China.

In addition, we have established intelligent workshop with all automatic equipment which is especially for export products.